Morphology of subsurface cracks in glass-ceramics induced by Vickers indentation observed by synchrotron X-ray

Gaku Okuma1, Kei Maeda2, Satoshi Yoshida3

  • 1Research Center for Structural Materials, National Institute for Materials Science, 1-2-1 Sengen, Tsukuba, Ibaraki, 305-0047, Japan. OKUMA.Gaku@nims.go.jp.

Scientific Reports
|April 28, 2022
PubMed

More Related Videos

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material07:42

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Published on: December 20, 2024

475
Full-field Strain Measurements for Microstructurally Small Fatigue Crack Propagation Using Digital Image Correlation Method07:37

Full-field Strain Measurements for Microstructurally Small Fatigue Crack Propagation Using Digital Image Correlation Method

Published on: January 16, 2019

9.8K

Related Concept Videos

Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
222
Types of Non-structural Cracks in Concrete01:28

Types of Non-structural Cracks in Concrete

Non-structural cracks are primarily of three types: plastic, early-age thermal, and drying shrinkage cracks. Plastic cracks are further classified into plastic shrinkage cracks and plastic settlement cracks.
Plastic shrinkage cracks typically form within hours after the concrete is poured. The concrete's surface dries faster than the bottom, creating tensile stress that the still-plastic concrete cannot withstand, leading to diagonal or randomly patterned cracks on the concrete surface.
260
X-ray Diffraction of Biological Samples01:10

X-ray Diffraction of Biological Samples

X-ray diffraction or XRD is an analytical tool that utilizes X-rays to study ordered structures such as crystalline organic and inorganic samples, polycrystalline materials, proteins, carbohydrates, and drugs.
According to Bragg's law, when X-rays strike the sample positioned on a stage, the rays are  scattered by the electron clouds around the sample atoms. The  X-ray diffraction or scattering is caused by constructive interference of the X-ray waves that reflect off the internal...
4.1K