Experimental study on fabrication, biocompatibility and mechanical characterization of polyhydroxybutyrate-ball clay...

The poly (3-hydroxybutyrate) (PHB)/ball clay nanocomposites (B1-B10) were synthesized using solvent casting method with different weight percentage of ball clay in PHB matrix. Scanning electron microscope (SEM) showed maximum root mean square roughness (188.73 μm) for 10% ball clay loading. Fourier transforms infrared spectroscopy (FT-IR) and X-ray diffraction (XRD) showed establishment of intercalated structure and formation of hydrogen bond between ball clay and PHB matrix. Contact angle values (67.3 - 51.3°) exhibited that the nanocomposites (B1-B10) are more hydrophilic than neat PHB (70.30°). Thermogravimetric (TGA) and differential scanning calorimetry (DSC) revealed maximum T_max (278 °C) and T_m (175 °C) for the nanocomposite B10 (PHB/PEG/ball clay: 80%/10%/10%). Maximum tensile strength (38.21 ± 0.15 MPa) and Young's modulus (1.74 ± 0.016 GPa) was observed for B10 nanocomposite. The values of protein adsorption, platelet adhesion, PT, APTT and complement activation for B10 nanocomposites were 165 ± 2 μg/cm², 72 ± 3 × 10⁹ platelets/cm², 23 ± 1 s, 44 ± 2 s, 102 ± 2 mg/dL and 631 ± 3 mg/dL, respectively. Hydroxyapatite formation was also observed for nanocomposite (B10) in in vitro simulated body fluid (SBF) study. Finally, the nanocomposite (B10) showed no harmful effect on MG-63 cells, indicating that they are physiologically safe.