A study on the effect of four thermoplastic elastomers on the properties of double-base propellants

Xiaobin Zou1, Wenguo Zhang1, Yongjun Gu2

  • 1School of Materials Science and Engineering, Beijing Institute of Technology Beijing 100081 China gzandlsy@bit.edu.cn yjluo@bit.edu.cn +86-10-68911608 +86-10-68911608.

RSC Advances
|May 6, 2022
PubMed

More Related Videos

Synthesis of Soft Polysiloxane-urea Elastomers for Intraocular Lens Application11:49

Synthesis of Soft Polysiloxane-urea Elastomers for Intraocular Lens Application

Published on: March 8, 2019

12.8K
The Preparation and Properties of Thermo-reversibly Cross-linked Rubber Via Diels-Alder Chemistry07:02

The Preparation and Properties of Thermo-reversibly Cross-linked Rubber Via Diels-Alder Chemistry

Published on: August 25, 2016

13.8K

Related Concept Videos

Polymer Classification: Stereospecificity01:26

Polymer Classification: Stereospecificity

Polymerization generates chiral centers along the entire backbone of a polymer chain. Accordingly, the stereochemistry of the substituent group has a significant effect on polymer properties. Polymers formed from monosubstituted alkene monomers feature chiral carbons at every alternate position in the polymer backbone. Relative to the predominant orientation of substituents at the adjacent chiral carbons, the polymer can exist in three different configurations: isotactic, syndiotactic, and...
2.7K
Polymer Classification: Architecture01:14

Polymer Classification: Architecture

Polymers are classified as linear or branched on the basis of their chain architecture. The polymer chains in linear polymers have a long chain-like structure with minimal to no branching at all. Even if a polymer features large substituent groups on the monomer, which appear as branches to the skeleton, it is not considered a branched polymer. A branched polymer contains secondary polymer chains that arise from the main polymer chain. The branching occurs when the polymer growth shifts from...
3.1K
Free-Radical Chain Reaction and Polymerization of Alkenes02:35

Free-Radical Chain Reaction and Polymerization of Alkenes

The conversion of alkenes to macromolecules called polymers is a reaction of high commercial importance. The structure of the polymer is defined by a repeating unit, while the terminal groups are considered insignificant. The average degree of polymerization represents the number of repeating units in the polymer molecule and is denoted by the subscript n.
8.3K
Types of Step-Growth Polymers: Polyesters01:20

Types of Step-Growth Polymers: Polyesters

The introduction of polyesters has brought major development to the textile industry. The wrinkle-free behavior of polyester blends has eliminated the need for starching and ironing clothes.
Polyesters are commonly prepared from terephthalic acid and ethylene glycol; the crude product is known as poly(ethylene terephthalate) or PET. However, polyesters are synthesized industrially by transesterification of dimethyl terephthalate with ethylene glycol at 150 °C. The two reactants and the...
2.3K
Olefin Metathesis Polymerization: Overview01:13

Olefin Metathesis Polymerization: Overview

Recently, the development of olefin metathesis polymerization advanced the field of polymer synthesis. Simply put, the reorganization of substituents on their double bonds between two olefins in the presence of a catalyst is known as the olefin metathesis reaction. The use of metathesis reaction for polymer synthesis is called olefin metathesis polymerization.
Ruthenium-based Grubbs catalyst is the most commonly used catalyst for olefin metathesis polymerization. Grubbs catalyst consists...
2.3K
Physical Properties of Alkanes02:33

Physical Properties of Alkanes

Alkanes are nonpolar molecules due to the presence of only carbon and hydrogen atoms. The electronegativity difference between carbon and hydrogen is minimal, and hence alkanes have a zero dipole moment. This leads to the presence of only dispersion forces between the molecules. The strength of dispersion forces is dependent on the surface area of the molecules on which they act. Since the surface area increases with the molecular length for straight-chain alkanes, the dispersion forces also...
12.5K