Zero-valent iron/activated carbon microelectrolysis to activate peroxydisulfate for efficient degradation of...

Tetracycline antibiotics are widely used in human and veterinary medicine; however, their gradual increase in the aquatic environment poses a serious threat to human health and ecosystems. The reactivity of peroxydisulfate (PDS) in the degradation of chlortetracycline (CTC) in aqueous solution using a zero-valent iron/activated carbon (AC) microelectrolysis method (Fe⁰-AC/PDS) was investigated by batch experiments. The results showed that the effects of different systems were as follows: Fe⁰-AC/PDS > Fe⁰/PDS > AC/PDS > Fe⁰-AC > AC > Fe⁰ > PDS. In the Fe⁰-AC/PDS system, the degradation efficiency of CTC could reach 88% under the following optimal experimental conditions: Fe⁰ dose of 0.4 g L^-1, PDS dose of 2 g L^-1, pH of 3 and initial CTC concentration of 50 mg L^-1. The presence of Cl^-, HCO₃ ^- and H₂PO₄ ^- inhibited the degradation of CTC, while humic acid accelerated the degradation rate of CTC. The mineralization of CTC was evaluated from the TOC, with a value of 31.44% in 7 h. Free radical identification experiments showed that SO₄ ^-˙ and O₂ ^-˙ were involved in the degradation of CTC. The iron and carbon materials had good reusability, and the degradation rate of CTC was still approximately 70% after four cycles. Finally, the possible mechanism for the degradation of CTC by the Fe⁰-AC/PDS systems was discussed. Based on the above conclusions, Fe⁰-AC microelectrolysis is a new heterogeneous catalytic method for green and efficient activation of PDS and demonstrates potential applicability in the treatment of wastewater.