Strong correlation between flux pinning and epitaxial strain in the GdBa2Cu3O7- /La0.7Sr0.3MnO3 nanocrystalline
1Department of Physics, Chungbuk National University Cheongju Korea bwkang@chungbuk.ac.kr +82 43 274 7811 +82 43 261 3394.
Abstract:
The effect of magnetic flux pinning is investigated in GdBa2Cu3O7 (GdBCO) thin films with two different types of ferromagnetic La0.7Sr0.3MnO3 (LSMO) buffers (nanoparticles and a layer) deposited on an STO substrate. Magnetization analyses reveal the presence of multiple flux pinning mechanisms responsible for the improvement in the critical current density of GdBCO films. While core pinning becomes a dominant pinning mechanism in GdBCO films with LSMO nanoparticles, a hybrid effect of magnetic-volume and core-point pinning is observed in GdBCO films with LSMO layers. Examinations of local structures for both LSMO and GdBCO using extended X-ray absorption fine structure spectroscopy (EXAFS) exhibit a close relation between the parameters in the pinning force scaling and the length ratio of the Mn-O bond to the Cu-O bond. This result implies that the origin of core pinning is probably attributed to epitaxial strain induced by lattice mismatch between LSMO and GdBCO. Therefore, an appropriate strain state of LSMO is required for an effective operation of magnetic pinning.
More Related Videos
Related Concept Videos
01:29Three-Dimensional Analysis of Strain
01:24Stress-Strain Diagram - Ductile Materials
03:02Colors and Magnetism
When atoms or molecules absorb light at the proper frequency, their electrons are excited to higher-energy orbitals. For many main group atoms and molecules, the absorbed photons are in the ultraviolet range of the electromagnetic spectrum, which cannot be detected by the human eye. For coordination compounds, the energy difference between the d orbitals often allows photons in the visible range to be absorbed and emitted, which is seen as colors by the human...