Novel magnetically separable anhydride-functionalized Fe₃O₄@SiO₂@PEI-NTDA nanoparticles as effective adsorbents:...

In this paper, a novel adsorbent, Fe₃O₄@SiO₂@PEI-NTDA, was first prepared by the immobilization of an amine and anhydride onto magnetic Fe₃O₄@SiO₂ nanoparticles with polyethylenimine (PEI) and 1,4,5,8-naphthalenetetracarboxylic-dianhydride (NTDA) for the removal of heavy metal ions from aqueous solutions. The structure of Fe₃O₄@SiO₂@PEI-NTDA was systematically investigated; the results confirmed that amine and anhydride groups were successfully covalently grafted onto the surface of Fe₃O₄@SiO₂, which showed a homogenous core-shell structure with three layers of about 300 nm diameter (Fe₃O₄ core: 200 nm, nSiO₂ layer: 20 nm, and PEI-NTDA layer: 20 nm). The adsorption performance of Fe₃O₄@SiO₂@PEI-NTDA NPs was evaluated for single Pb²⁺ and coexisting Cd²⁺, Ni²⁺, Cu²⁺, and Zn²⁺ ions in an aqueous solution in a batch system. The amine and anhydride groups may have a synergistic effect on Pb²⁺ removal through electrostatic interactions and chelation; Fe₃O₄@SiO₂@PEI-NTDA NPs exhibited preferable removal of Pb²⁺ with maximum adsorption capacity of 285.3 mg g^-1 for Pb²⁺ at a solution pH of 6.0, adsorbent dosage of 0.5 g L^-1, initial Pb²⁺ concentration of 200 mg L^-1 and contact time of 3 h. The adsorption mechanism conformed well to the Langmuir isotherm model, and the adsorption kinetic data were found to fit the pseudo-second order model. Fe₃O₄@SiO₂@PEI-NTDA NPs could be recovered easily from their dispersion by an external magnetic field and demonstrated good recyclability and reusability for at least 6 cycles with a high adsorption capacity above 204.5 mg g^-1. The magnetic adsorbents showed high stability with a weight loss below 0.65% in the acid leaching treatment by 2 M HCl solution for 144 h. This study indicates that Fe₃O₄@SiO₂@PEI-NTDA NPs are new promising adsorbents for the effective removal of Pb²⁺ in wastewater treatment.