Atomic layer deposition with rotary reactor for uniform hetero-junction photocatalyst, g-C₃N₄@TiO₂ core-shell...

A heterojunction of TiO₂ grown on g-C₃N₄ particles is demonstrated using atomic layer deposition (ALD), equipped with a specifically designed rotary reactor for maintaining stable mechanical dispersion of g-C₃N₄ particles during ALD. The photocatalytic activity of the g-C₃N₄@ALD-TiO₂ core-shell composites was examined using the degradation of rhodamine B dye under visible light irradiation. The optimal composite with 5 ALD cycles of TiO₂ exhibited the highest photocatalytic reaction rate constant among the composites with a range of ALD cycles from 2 to 200 cycles, which was observed to be 3 times higher than that of pristine g-C₃N₄ and 2 times higher than that of g-C₃N₄@TiO₂ composite prepared using a simple impregnation method. The ALD-TiO₂ were well-dispersed on the g-C₃N₄ surface, while TiO₂ nanoparticles were agglomerated onto the g-C₃N₄ in the g-C₃N₄@TiO₂ composite prepared by the impregnation method. This created uniform and stable heterojunctions between the g-C₃N₄ and TiO₂, thus, enhancing the photocatalytic activity.