Unexpected visible light driven photocatalytic activity without cocatalysts and sacrificial reagents from a (GaN)_1-...

Optical and photocatalytic properties were determined for the solid solution series (GaN)_1- (ZnO) synthesized at high pressure over the entire compositional range (x = 0.07 to 0.9). We report for the first time photocatalytic H₂ evolution activity from water for (GaN)_1- (ZnO) without cocatalysts, pH modifiers and sacrificial reagents. Syntheses were carried out by reacting GaN and ZnO in appropriate amounts at temperatures ranging from 1150 to 1200 °C, and at a pressure of 1 GPa. ZnGa₂O₄ was observed as a second phase, with the amount decreasing from 12.8 wt% at x = 0.07 to ∼0.5 wt% at x = 0.9. The smallest band gap of 2.65 eV and the largest average photocatalytic H₂ evolution rate of 2.31 μmol h^-1 were observed at x = 0.51. Samples with x = 0.07, 0.24 and 0.76 have band gaps of 2.89 eV, 2.78 eV and 2.83 eV, and average hydrogen evolution rates of 1.8 μmol h^-1, 0.55 μmol h^-1 and 0.48 μmol h^-1, respectively. The sample with x = 0.9 has a band gap of 2.82 eV, but did not evolve hydrogen. An extended photocatalytic test showed considerable reduction of activity over 20 hours.