Quantitative characterization of the long-term charge storage of a ZnO-based nanorod array film through persistent...

The persistent nature of the increased conductivity upon removal of incident illumination, described by the term persistent photoconductivity (PPC), in ZnO films is sensitive to their defect states. PPC can be viewed as a process of charge storage with relevant defects. To evaluate charge storage quantitatively, in this work, some thought-provoking characteristic quantities were derived from a photocurrent-time curve acquired by testing the photoelectric properties of ZnO under on and off UV illumination. Q _uo was defined as the obtained charge number per unit voltage during the light-on phase, while Q _us was defined as the storage charge number during the light-off phase. η was acquired by dividing Q _us by Q _uo to measure the storage efficiency after the removal of UV light. On the basis of previous work, it was assumed that the PPC of ZnO originated from the unique property of V⁰ _O. Meanwhile, this report reveals that the intrinsic defects V_O ²⁺, V_O ⁺, V⁰ _Zn will enhance Q _uo and Q _us but decrease η in the pure ZnO nanorod array film. The extrinsic defect Cu⁰ _Zn introduced by coating the ZnO nanorod array film in an ethanol solution of copper acetate suppresses Q _uo and Q _us but promotes the increase of η. Since the whole methodology originated from a series of physical definitions, it can be easily extended to other materials with similar PPC effects.