Inkjet printing of blue phosphorescent light-emitting layer based on bis(3,5-di(9H-carbazol-9-yl))diphenylsilane

In this study, micropatterning of a blue light emitting, tetraphenylsilane-based phosphorescent material by inkjet printing was investigated. Bis(3,5-di(9H-carbazol-9-yl))diphenylsilane (SimCP2) doped with iridium bis(4,6-difluorophenypyridinato)picolate (FIrpic) was dissolved in a solvent mixture, and various conditions for the solvent composition and drying of films were examined. Homogeneous dot and line patterns with controllable thickness and smooth surface were obtained from a mixture of chlorobenzene and cyclohexanone at a moderate printing speed of 3 mm s^-1 and a droplet ejection frequency of 70 Hz. An inkjet-printed device was designed and fabricated in [ITO/PEDOT:PSS /PVK/SimCP2:Flrpic/TSPO1/TPBi/LiF/Al] configuration, from which sky-blue light (0.14, 0.25) was obtained with a luminous efficiency of 10.73 cd A^-1 and a power efficiency of 6.13 lm W^-1. This amounted to 68% of the performance of an identical device where the emitting layer was spin coated. These results show the potential of inkjet printing as a low-cost patterning method for low molecular weight emitters in blue light emitting devices.