Ag decorated silica nanostructures for surface plasmon enhanced photocatalysis

In this article, we present a novel synthesis of mesoporous SiO₂/Ag nanostructures for dye (methylene blue) adsorption and surface plasmon mediated photocatalysis. Mesoporous SiO₂ nanoparticles with a pore size of 3.2 nm were synthesized using cetyltrimethylammonium bromide as a structure directing agent and functionalized with (3-aminopropyl)trimethoxysilane to introduce amine groups. The adsorption behavior of non-porous SiO₂ nanoparticles was compared with that of the mesoporous silica nanoparticles. The large surface area and higher porosity of mesoporous SiO₂ facilitated better adsorption of the dye as compared to the non-porous silica. Ag decorated SiO₂ nanoparticles were synthesized by attaching silver (Ag) nanoparticles of different morphologies, i.e. spherical and triangular, on amine functionalized silica. The photocatalytic activity of the mesoporous SiO₂/Ag was compared with that of non-porous SiO₂/Ag nanoparticles and pristine Ag nanoparticles. Mesoporous SiO₂ nanoparticles (k _d = 31.3 × 10^-3 g mg^-1 min^-1) showed remarkable improvement in the rate of degradation of methylene blue as compared to non-porous SiO₂ (k _d = 25.1 × 10^-3 g mg^-1 min^-1) and pristine Ag nanoparticles (k _d = 19.3 × 10^-3 g mg^-1 min^-1). Blue Ag nanoparticles, owing to their better charge carrier generation and enhanced surface plasmon resonance, exhibited superior photocatalysis performance as compared to yellow Ag nanoparticles in all nanostructures.