Synthesis of ordered Ca- and Li-doped mesoporous silicas for H₂ and CO₂ adsorption at ambient temperature and pressure

Ca- and Li-doped mesoporous silicas have been prepared successfully using cetyltrimethylammonium bromide (CTAB) surfactant in basic media. Sol-gel synthesis and hydrothermal treatment produced highly ordered mesoporous Ca and Li loaded silica particles. The MCM-41 type mesostructures, the porosity, the pore sizes as well as the surface area of Ca- and Li-silicas have been thoroughly investigated using small angle X-ray scattering (SAXS), transmission electron microscopy (TEM), and N₂ sorption analysis. Samples prepared with varying amounts of Li and Ca loading have been further analyzed using inductive coupled plasma-atomic emission spectroscopy (ICP-AES) and field-emission scanning electron microscopy (FESEM) with an energy dispersive spectral attachment (EDS), which confirmed quite a large amount of Ca while the amount of Li was not enough. Additionally, H₂ and CO₂ gas uptake studies of these metal-loaded silicas have been carried out using a thermogravimetric analyzer (TGA) at normal temperature (25 °C) and pressure (1 atm). H₂ uptake of up to 10 mmol g^-1 by Ca-doped silica was recorded. CO₂ and H₂ selectivity were tested with both pure metal-MCM-41 and amine loaded silica using pure N₂ gas and a mixed flow of CO₂/N₂ and H₂/N₂. The effect of temperature on CO₂ uptake was also studied using Ca-MCM-41 materials.