Composite design bioinspired by the mesocarp of Brazil nut (Bertholletia excelsa)

The mesocarp ofBertholletia excelsais a rich source of inspiration for strong, stiff and damage-tolerant composites. The bioinspired composites developed here are composed of an epoxy matrix with a 3D printed polylactic acid reinforced with 30% of carbon fiber (PLA-30CF) inspired in fibers, and syntactic foam inspired by sclereids. Monotonic and cyclic four-point bending tests and compact tension fracture toughness tests were carried out assisted by digital image correlation (DIC) to evaluate flexural properties, damage tolerance, and theR-curve of the composite. Its microstructure and fracture surface were analyzed by scanning electron microscopy. The mechanical performance of the bioinspired composite is promising: density of 1.0 g cm^-3, flexural apparent elastic modulus of 1.6 GPa, and flexural strength six times higher than the neat epoxy, i.e. 17 MPa. Although the PLA-30CF printed structure led to a risingR-curve, the syntactic foam needs optimization to have a synergistic effect.