A General Way to Fabricate Chain-like Ferrite with Ultralow Conductive Percolation Threshold and Wideband Absorbing...

The magnetic nanochain-like material has been regards as one of the most promising electromagnetic (EM) absorbing material but remains a challenging. Herein, magnetic chain-like ferrite (included Fe₃O_4, CoFe₂O₄ and NiFe₂O₄) are successfully produced through a general solvothermal method, using PVP as the structural-liking agent. Experimental results confirm the ultimate sample possess a 3-dimensional chain-like structure which are constructed by numerous ferrite's nanoparticles with ~60 nm in diameter. Their electromagnetic parameters can be also manipulated by such a chain structure, especially the dielectric loss, where a sharply increases can be observed on within a lower filling ratio. It greatly benefits to the EM absorbing property. In this article, the electromagnetic absorption layer made with a lower content of ferrite possess the excellent electromagnetic absorption ability, where the optimized effective absorption band was nearly 6.4 GHz under a thickness of 1.8 mm. Moreover, the filling ratio is only 30 wt%. Our method for designing of chain-like magnetic material can be helpful for producing wideband electromagnetic absorption in a low filling ratio.