Encapsulation and Permeability Characteristics of Plasma Polymerized Hollow Particles
Published on: August 16, 2012
Experimental Research on Seepage Law and Migration Characteristics of Core-Shell Polymeric Nanoparticles Dispersion
Xiaohe Huang1,2, Yuyi Wang1, Yunqian Long1,2
1School of Petrochemical Engineering & Environment, Zhejiang Ocean University, Zhoushan 316022, China.
Abstract:
The nanoparticles dispersion system has complex migration characteristics and percolation law in porous media due to the interaction between the nanoparticles and porous media. In this paper, lab experiments were carried out to characterize the morphology, particle size distributions, and apparent viscosities of SiO2/P(MBAAm-co-AM) polymeric nanoparticle solution, investigate its migration characteristics in porous media, and probe its capability of enhanced oil recovery (EOR) in the reservoirs. Quartz microtubule, sand pack, and etched glass micromodels were used as the porous media in the flow and flooding experiments. Gray image-processing technology was applied to achieve oil saturation at different flooding stages in the micromodel for calculating the EOR of the SiO2/P(MBAAm-co-AM) polymeric nanoparticle solution. The results show that The SiO2/P(MBAAm-co-AM) polymeric nanoparticles are spherical with diameters ranging from 260 to 300 nm, and the thicknesses of the polymeric layers are in the range of 30-50 nm. As the swelling time increases from 24 to 120 h, the medium sizes of the SiO2/P(MBAAm-co-AM) polymeric nanoparticles increase from 584.45 to 1142.61 nm. The flow of the SiO2/P(MBAAm-co-AM) polymeric nanoparticles has obvious nonlinear characteristics and a prominent scale effect at a low-pressure gradient, and there should be an optimal matching relationship between its injection mass concentration and the channel size. The flow tests in the sand packs demonstrate that the SiO2/P(MBAAm-co-AM) polymeric nanoparticles can form effective plugging in the main flow channels at different permeability areas and can break through at the throat to fulfill the step-by-step profile control. Moreover, the profile control of the SiO2/P(MBAAm-co-AM) polymeric nanoparticles strengthens with an increase in their swelling time. The microscopic flooding experiment in the etched glass micromodel confirms that the SiO2/P(MBAAm-co-AM) polymeric nanoparticles can block dynamically and alternatively the channels of different sizes with the form of loose or dense networks to adjust the fluid flow diversion, improve the sweep efficiency, and recover more residual oil. The SiO2/P(MBAAm-co-AM) polymeric nanoparticles can achieve an enhanced oil recovery of 20.71% in the micromodel.
More Related Videos
06:01Frugal Imaging Technique of Capillary Flow Through Three-Dimensional Polymeric Printing Powders
Published on: October 4, 2022
11:23Polydimethylsiloxane-polycarbonate Microfluidic Devices for Cell Migration Studies Under Perpendicular Chemical and Oxygen Gradients
Published on: February 23, 2017
Related Concept Videos
01:25Permeability of Concrete
01:20Porosity and Absorption of Aggregate
When all pores in an aggregate are filled with water, the aggregate is considered saturated and surface-dry. If left in dry air, water will evaporate until the...
01:08Molecular Weight of Step-Growth Polymers
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...