The Effect of Two Different Light-Curing Units and Curing Times on Bulk-Fill Restorative Materials

This study aimed to evaluate the effect of two different light-curing units and curing times on the surface microhardness (SMH), compressive strength (CS), and volumetric shrinkage (VS) of four restorative materials (Filtek^TM Z250, Filtek^TM Bulk Fill Posterior, Beautifil^® Bulk Restorative, ACTIVA^TM BioACTIVE). For all tests, each material was divided into two groups depending on the curing unit (Woodpecker LED-E and CarboLED), and each curing unit group was further divided into two subgroups according to curing time (10 s and 20 s). SMH was evaluated using a Vickers hardness tester, CS was tested using a universal testing machine, and VS was measured using video imaging. In all the restorative materials cured with Woodpecker LED-E, the 20 s subgroup demonstrated significantly higher SMH values than the 10 s subgroup. In both light-curing time subgroups, the CarboLED group showed significantly higher CS values than the Woodpecker LED-E group for all restorative materials except Filtek^TM Bulk Fill Posterior cured for 20 s. ACTIVA^TM BioACTIVE showed significantly greater volumetric change than the other restorative materials. A higher curing light intensity and longer curing time had a positive effect on the SMH and CS of the restorative materials tested in this study. On the other hand, curing unit and time did not show a significant effect on the VS values of restorative materials.