Preparation of Bismuth Tungstate/Preoxidized Acrylonitrile/Acrylic Acid Copolymer Composite Nanofiber Membrane and
Yinchun Fang1, Xinhua Liu1,2, Hongzhang Li1
1School of Textile and Garment, Anhui Polytechnic University, Wuhu 241000, China.
Background:
In this patent article, a novel bismuth tungstate/preoxidized acrylonitrile/ acrylic acid (AN/AA) copolymer composite nanofiber membrane was prepared, which was used as the visible light catalyst.
Methods:
AN/AA copolymer was synthesized, which was electrospun with bismuth nitrate and sodium tungstate to prepare the composite nanofiber. Then the composite nanofiber was preoxidized to prepare the bismuth tungstate/preoxidized AN/AA composite nanofiber membrane containing adsorption moiety and photocatalytic active moiety.
Results:
The photocatalytic activity of bismuth tungstate/preoxidized AN/AA composite nanofiber membrane with different preoxidized temperature, heating rate, and holding time by catalytic degradation of methylene blue was investigated. The optimal preoxidized conditions were as follows: the preoxidized temperature was heated to 200 °C with the heating rate of 1°C/min and the holding time at this temperature was 12 h. The chemical structure and morphology of the composite nanofiber membrane were characterized by FTIR, XRD, and SEM.
Conclusion:
The bismuth tungstate/preoxidized AN/AA composite nanofiber membrane obtained good photocatalytic properties and reusability under visible light. The degradation rate of methylene blue by this visible light catalyst could reach 90.24% for 4.5 h, and the degradation rate remained 81.53% for 4.5 h after 5 reuses.
More Related Videos
12:00Preparation of Light-responsive Membranes by a Combined Surface Grafting and Postmodification Process
Published on: March 21, 2014
12:47Preparation and Use of Photocatalytically Active Segmented Ag|ZnO and Coaxial TiO2-Ag Nanowires Made by Templated Electrodeposition
Published on: May 2, 2014