Atomic Force Microscopy Observation of Polylactide Stereocomplex Edge-On Crystals in Thin Films: Effects of Molecular Weight on Lamellar Curvature
Related Experiment Video
Updated: Sep 22, 2025
Methods for the Self-integration of Megamolecular Biopolymers on the Drying Air-LC Interface
Published on: April 7, 2017
Hironori Marubayashi1, Toshihiro Nobuoka1, Shinichiro Iwamoto1
1Science of Polymeric Materials, Department of Biomaterial Sciences, Graduate School of Agricultural and Life Sciences, The University of Tokyo, 1-1-1 Yayoi, Bunkyo-ku, Tokyo 113-8657, Japan.
Abstract:
The shapes of the edge-on lamellar crystals of equiweight poly(l-lactide) (PLLA)/poly(d-lactide) (PDLA) stereocomplexes with various combinations of molecular weights were investigated by using atomic force microscopy. In the cases of the PLLA/PDLA blends with equivalent molecular weights, the straight-shaped edge-on lamellae were observed. On the other hand, the curved edge-on crystals were able to be seen for the PLLA/PDLA stereocomplexes with nonequivalent molecular weights. It was revealed that the direction of lamellar curvature in the polylactide (PLA) stereocomplexes with nonequivalent molecular weights is the same as that of PLA having lower molecular weight. In addition to the PLLA/PDLA blending ratio, the incidence of chain folding, which is strongly influenced by molecular weight, was considered to have a crucial effect on the lamellar curvature in the edge-on crystals of PLA stereocomplexes.
More Related Videos
11:26Towards Biomimicking Wood: Fabricated Free-standing Films of Nanocellulose, Lignin, and a Synthetic Polycation
Published on: June 17, 2014
09:43Interfacial Molecular-level Structures of Polymers and Biomacromolecules Revealed via Sum Frequency Generation Vibrational Spectroscopy
Published on: August 13, 2019
Related Concept Videos
01:08Molecular Weight of Step-Growth Polymers
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...
01:21Polymer Classification: Crystallinity
Crystalline domains are the regions where polymer chains are aligned in an orderly manner and held together in proximity by intermolecular forces. For example, chains in the crystalline domains of polyethylene and nylon are bound together by van der Waals...