The Effect of the Heating Rate during Carbonization on the Porosity, Strength, and Electrical Resistivity of Graphite

Sang-Hye Lee1, Jae-Hyun Kim2, Woo-Seok Kim2

  • 1School of Materials Science and Engineering, Kumoh National Institute of Technology, Gumi 39177, Korea.

Materials (Basel, Switzerland)
|May 20, 2022
PubMed

Keywords:
carbonizationelectrical resistivitygraphite blockheating ratemechanical propertymicrostructurephenolic resinporositythermal decomposition

More Related Videos

Negative Additive Manufacturing of Complex Shaped Boron Carbides06:45

Negative Additive Manufacturing of Complex Shaped Boron Carbides

Published on: September 18, 2018

8.8K
Effect of Bending on the Electrical Characteristics of Flexible Organic Single Crystal-based Field-effect Transistors08:43

Effect of Bending on the Electrical Characteristics of Flexible Organic Single Crystal-based Field-effect Transistors

Published on: November 7, 2016

8.1K

Related Concept Videos

Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is...
238
Resistivity01:22

Resistivity

When a voltage is applied to a conductor, an electrical field is generated, and charges in the conductor feel the force due to the electrical field. The current density that results depends on the electrical field and the properties of the material. In some materials, including metals at a given temperature, the current density is approximately proportional to the electrical field. In these cases, the current density can be modeled as:
3.7K
Strength and Heat of Hydration01:29

Strength and Heat of Hydration

The hydration of cement is an exothermic reaction in which heat is generated as cement hydrates. This heat of hydration is critical to cement's strength development. The rate at which this heat is generated affects the temperature rise, with a majority of the heat being released early in the hydration process, half within the first three days, and about 75% within the first week.
The heat of hydration for each cement compound is significant; for instance, tricalcium aluminate (C3A) and...
362
Pore Size Distribution01:23

Pore Size Distribution

In concrete, the pore size distribution significantly influences the material's properties. Capillary pores, markedly larger than gel pores, form a vast network within partially hydrated cement paste, reducing the concrete's strength and increasing its permeability. This heightened permeability leads to a greater risk of damage from environmental factors like freeze-thaw cycles and chemical attacks, with the extent of vulnerability also being tied to the water-to-cement ratio.
Adequate...
222