Color Changes Associated with Sandblasting, Hydrofluoric Acid Etching, and Er:YAG Laser Irradiation of Milled...

To evaluate color changes in milled feldspathic porcelain laminate veneers following hydrofluoric acid etching (HFA), sandblasting (SB), or Er:YAG laser irradiation (LI).

Disc-shaped specimens (thickness=1 mm, diameter=8 mm) were milled from feldspathic porcelain blocks (n=40). Glazed specimens were randomly assigned to four subgroups (n=10 each) according to surface treatment: negative control, HFA, SB, and LI. A layer of translucent, light-cured resin cement (thickness=0.1 mm) was then applied following silanization. The color was characterized by the L*, a*, and b* uniform color space (CIE) using a reflection spectrophotometer. CIEDE2000 (ΔE00) was calculated to determine the color difference between each surface treatment and negative control groups. Data were statistically analyzed using analysis of variance (ANOVA), Kruskal-Wallis, and Dunn-Bonferroni post hoc tests.

There were no significant differences in CIEL* and CIEb* coordinates between negative control and all surface treatment groups (p≥0.108). The SB group demonstrated significantly lower mean CIEa* (higher greenish hue) compared to other groups (p≤0.003). HFA exhibited significantly higher CIEa* (closer to red) when compared to LI (p=0.039). LI induced the smallest overall color change compared to negative control (ΔE00=1.43 [1.07]). However, the differences in ΔE00 values were not statistically significant (p=0.648).

The tested surface treatments did not affect the lightness or the yellowness of the 1-mm-thick milled feldspathic porcelain veneers. However, sandblasting resulted in a significant increase in the greenish hue. The Er:YAG laser resulted in the closest ΔE00 (1.43) to the 50:50% perceptibility threshold (ΔE00=1.2).