Impact of Fabrication Techniques and Polishing Procedures on Surface Roughness of Denture Base Resins
Published on: January 17, 2025
Evaluation of Shear Bond Strength Between Denture Teeth and 3D-Printed Denture Base Resin
Marília P Cleto1, Marcela D D Silva1, Thaís S B S Nunes1
1Department of Dental Materials and Prosthodontics, Araraquara Dental School, Univ Estadual Paulista (UNESP), Araraquara, São Paulo, Brazil.
Purpose:
The aim of this study was to evaluate the bond strength between two types of artificial teeth with a 3D-printed denture base resin using different bonding agents.
Materials And Methods:
Two types of artificial teeth were evaluated: 3D-printed (Cosmos TEMP) and prefabricated polymethylmethacrylate (Biotone) bonded to cylinders (2.5 mm in height and 5 mm in diameter) of 3D-printed denture bases (Cosmos Denture designing by Meshmixer and printed by Flashforge Hunter DLP Resin 3D Printer). Two combinations between denture base and artificial teeth were eveluated: Cosmos Denture - Biotone, n = 30, and Cosmos Denture - Cosmos TEMP, n = 30. For each combination, the specimens were randomly distributed according to the bonding agent: (1) autopolymerized acrylic resin-Duralay, n = 10; (2) 3D-printed resin Cosmos TEMP, n = 10; and (3) methylmethacrylate monomer (MMA) + 3D-printed resin Cosmos TEMP, n = 10, totaling 60 specimens. The application of MMA was done conditioning the tooth surface for 180 seconds; the other agents were applied on the same surface. The virtual design of the 3D-printed resin teeth was obtained by scanning the first maxillary molar of the prefabricated teeth as the same protocol of cylinders. The control group (n = 10) was a conventional heat-polymerized denture base resin (Lucitone 550) bonded to the prefabricated resin teeth (Biotone). The shear bond tests were performed by applying a perpendicular force to the artificial tooth - denture base resin, through a chisel at 1 mm/min until failure. Two-way ANOVA and Bonferroni post hoc tests (α = 0.05) were used for multiple comparisons.
Results:
For the Biotone tooth, the bond strength was significantly higher using MMA + Cosmos TEMP (10.04 MPa), and similar to the control (11.84 MPa, p = 0.484). For the 3D-printed tooth (Cosmos TEMP), the bond strength using the agents Cosmos TEMP (9.57 MPa) and MMA + Cosmos TEMP (12.72 MPa) were similar to the control (11.84 MPa, p = 0.169 and p = 1, respectively), but different from each other (p = 0.016).
Conclusions:
From the results, it is recommended to use: MMA + Cosmos TEMP bonding agent for the Biotone tooth; and Cosmos TEMP or MMA + Cosmos TEMP bonding agents for the Cosmos TEMP tooth, both attached to the 3D-printed denture resin Cosmos Denture.