Robust Silica-Agarose Composite Aerogels with Interpenetrating Network Structure by In Situ Sol-Gel Process

Aerogels are three-dimensional nanoporous materials with outstanding properties, especially great thermal insulation. Nevertheless, their extremely high brittleness restricts their practical application. Recently, although the mechanical properties of silica aerogels have been improved by regulating the precursor or introducing a polymer reinforcer, these preparation processes are usually tedious and time-consuming. The purpose of this study was to simplify the preparation process of these composite aerogels. A silicic acid solution treated with cation exchange resin was mixed with agarose (AG) to gel in situ, and then composite aerogels (CAs) with an interpenetrating network (IPN) structure were obtained by aging and supercritical CO₂ fluid (SCF) drying. Compared to previous works, the presented CAs preparation process is briefer and more environmentally friendly. Moreover, the CAs exhibit a high specific surface area (420.5 m²/g), low thermal conductivity (28.9 mW m^-1 K^-1), excellent thermal insulation properties, and thermal stability. These results show that these CAs can be better used in thermal insulation.