Role of Liquid-Phase Amount in Ceramization of Silicone Rubber Composites and Its Controlling

The reliable mechanical properties of ceramizable silicone rubber composites during pyrolysis are necessary for their application in the fire-resistant fields. The effects of liquid-phase amount on the mechanical properties of silicone rubber composites are investigated. The results show a positive correlation between the liquid-phase amount and the flexural strength of the residual products pyrolysis below 800 °C. The nano-γ-Al₂O₃ in the fillers reacts with liquid B₂O₃ to form aluminum borate above 800 °C, which consumes the liquid phase and strengthens the residual products to a certain extent. Increasing the B₂O₃ addition and introducing nano-γ-Al₂O₃ can control the liquid-phase amount in the range of 15% to 30%, which makes the composites have better residual strength and support performance. The residual strength of composites pyrolysis at 500 °C to 1000 °C is higher than 2.50 MPa, and the maximum is up to 18.7 MPa at 1000 °C.