Green Composites from Partially Bio-Based Poly(butylene succinate-co-adipate)-PBSA and Short Hemp Fibers with...

In this work, green composites have been developed and characterized using a bio-based polymeric matrix such as BioPBSA and the introduction of 30 wt.% short hemp fibers as a natural reinforcement to obtain materials with maximum environmental efficiency. In order to increase the interfacial adhesion between the matrix and the fiber to obtain better properties in the composites, a reactive extrusion process has been carried out. On the one hand, different additives derived from bio-based itaconic acid have been added to the BioPBSA/HEMP composite, such as dibutyl itaconate (DBI) and a copolymer of PBSA grafted with itaconic acid (PBSA-g-IA). On the other hand, a different copolymer of PBSA grafted with maleic anhydride (PBSA-g-MA) was also tested. The resulting composites have been processed by injection-molding to obtain different samples which were evaluated in terms of mechanical, thermal, chemical, dynamic-mechanical, morphological and wettability and color properties. In relation to the mechanical properties, the incorporation of hemp fibers resulted in an increase in the stiffness of the base polymer. The tensile modulus of pure BioPBSA increased from 281 MPa to 3482 MPa with 30% fiber. The addition of DBI shows a remarkable improvement in the ductility of the composites, while copolymers with IA and MA, generate mechanically balanced composites. In terms of thermal properties, the incorporation of hemp fiber and compatibilizing agents led to a reduction in thermal stability. However, from the point of view of thermomechanical properties, a clear increase in rigidity is achieved throughout the temperature range studied. As far as the color of the samples is concerned, the incorporation of hemp generates a typical color, while the incorporation of the compatibilizing agents does not modify this color excessively. Finally, the introduction of lignocellulosic fibers greatly affects water absorption and contact angle, although the use of additives helped to mitigate this effect.