A Phosphorus-Nitrogen-Carbon Synergistic Nanolayered Flame Retardant for Polystyrene

Polymers are widely used in our daily life; however, most of them are highly flammable. Once modified with flame retardants (FRs), polymers always have deteriorative properties in mechanical strength aspects. As a countermeasure, a novel unified phosphorus and nitrogen-containing organic nano-layered flame retardant (BA-MA) was synthesized by the assembly of biphenyl-4,4'-diphosphonic acid (BA) and melamine (MA), which was used as an additive flame retardant for polystyrene (PS) resin. The chemical structure and morphology of BA-MA were characterized, and a possible growth mechanism of the nanolayered structure was presented in detail. The resulting BA-MA with a thickness of about 60 nm can be uniformly dispersed in the PS resin, thus maintaining the mechanical properties of the material. Remarkably, under only 1 wt% loading of BA-MA, the flammability of PS can be largely reduced with a 68% reduction in the peak heat release rate. Additionally, the smoke release was also significantly inhibited. The research on flame retardant mechanisms shows that BA-MA mainly produces incombustible gas to dilute the concentration of combustibles and promote the formation of aromatic carbon layers to isolate oxygen transmission and heat transfer.