Newly engineered alumina quantum dot-based nanofluid in enhanced oil recovery at reservoir conditions

In this work, a newly engineered alumina quantum dot-based nanofluid (α-AQDs; D ~ 4 nm; amorphous solid) and one commercial alumina nanoparticle-based nanofluid (γ-ANPs; D ~ 20 nm; crystalline type) with the capability of strong colloidal dispersion at reservoir conditions, such as, high salinity, divalent ions (Ca²⁺) and high temperature was compared. The main goal of this research was to study the crude oil displacement mechanisms of alumina suspensions as a function of variety in size and particle morphology in aged carbonate rocks. The strong interaction potential between the particles was achieved by the citric acid and a special composition of a carboxylate-sulfonate-based polyelectrolyte polymer as an effective dispersant compound on the surface, leading to a negative particle charges and an additional steric and electrostatic repulsion. Wettability alteration upon exposure to fluids using the contact angle and the Amott cell were performed on saturated carbonate plug samples and rock slices. While, dynamic core displacements were conducted to test the water/nanofluid/oil flow and nanoparticle retention behavior thorough typical pore throats underground the reservoir conditions. The stability results revealed that PE-polymer was able to create a long-term colloidal fluid during 30 days. It was found that mass concentration of nanofluid increased with decreasing in particle size. The optimal amount of particles in aqueous solution was obtained 0.05 wt% for ANPs, increased up to 0.1 wt% for AQDs. Analysis of experiments showed that wettability alteration was the main mechanism during nanofluid injection. Laboratory core-flooding data proved that the enhanced oil recovery due to a less concentration state by ANPs was consistent with AQDs at higher concentrations. In addition, permeability-impairment-behavior study was discussed in terms of possible mineral scale deposition and alumina release on the rock surface. Results showed that a large extent of permeability damage caused by mineral scale (55-59%). Alumina quantum dot-based nanofluids were found a minimum impairment (2-4%) and a significant reduction of ~ 10% in permeability was observed for ANPs-based nanofluid.