Damage Mechanisms and Anisotropy of an AA7010-T7452 Open-Die Forged Alloy: Fatigue Crack Propagation

The process-microstructure-property relationship of high-strength 7000 series aluminum alloys during fatigue crack propagation (FCP) is highly relevant for safety during the design and service of aircraft structural components. It is scientifically evident that many metallurgical factors affect FCP properties, but partly contradictory or inconclusive results show that the quantitative description of the relationships is still a major challenge among researchers and engineers. Most research focuses on sheet or plate products and investigations lack quantitative information on the process-property relationship between open-die forged thick products and FCP. The present study contributes to this field by investigating the fatigue crack growth behavior of an open-die forged AA7010-T7452 aluminum alloy. Four different forging conditions comprising different characteristic microstructures are comparatively analyzed. The influence of grain size, grain shape, specimen orientation, crystallographic texture, and primary phase particles is investigated. Fractographic analysis reveals different active damage mechanisms during fatigue crack growth. Based on that, the microstructure features relevant to fatigue damage areidentified in each regime of crack growth.