Flow Behavior of AA5005 Alloy at High Temperature and Low Strain Rate Based on Arrhenius-Type Equation and Back...

To realize the purpose of energy saving, materials with high weight are replaced by low-weight materials with eligible mechanical properties in all kinds of fields. Therefore, conducting research works on lightweight materials under specified work conditions is extremely important and profound. To understand the relationship of aluminum alloy AA5005 among flow stress, true strain, strain rate, and deformation temperature, hot isothermal tensile tests were conducted within the strain rate range 0.0003-0.03 s^-1 and temperature range 633-773 K. Based on the true stress-true strain curves obtained from the experiment, a traditional constitutive regression Arrhenius-type equation was utilized to regress flow behaviors. Meanwhile, the Arrhenius-type equation was optimized by a sixth-order polynomial function for compensating strain. Thereafter, a back propagation artificial neural network (BP-ANN) model based on supervised machine learning was also employed to regress and predict flow stress in diverse deform conditions. Ultimately, by introducing statistical analyses correlation coefficient (R²), average absolute relative error (AARE), and relative error (δ) to the comparative study, it was found that the Arrhenius-type equation will lose accuracy in cases of high stress. Additionally, owning higher R², lower AARE, and more concentrative δ value distribution, the BP-ANN model is superior in regressing and predicting than the Arrhenius-type constitutive equation.