Effect of Preheating Temperature on Geometry and Mechanical Properties of Laser Cladding-Based Stellite 6/WC Coating

The effect of 60Si2Mn substrate preheating on the forming quality and mechanical properties of cobalt-based tungsten carbide composite coating was investigated. Substrate preheating was divided into four classes (room temperature, 150 °C, 250 °C, and 350 °C). The morphology, microstructure, and distribution of elements of the coating were analyzed using a two-color laser handheld 3D scanner, a scanning electron microscope (SEM), and an energy dispersive X-ray spectrometer (EDX), respectively. The hardness and wear properties of the cladding layer were characterized through a microhardness tester and a friction wear experiment. The research results show that the substrate preheating temperature is directly proportional to the height of the composite coating. The solidification characteristics of the Stellite 6/WC cladding layer structure are not obviously changed at substrate preheating temperatures of room temperature, 150 °C, and 250 °C. The solidified structure is even more complex at a substrate preheating temperature of 350 °C. At this moment, the microstructure of the cladding layer is mainly various blocky, petaloid, and flower-like precipitates. The hardness and wear properties of the cladding layer are optimal at a substrate preheating temperature of 350 °C in terms of mechanical properties.