Synthesis and Characterization of Fluorite-Type La₂Ce₂O₇ Plasma Sprayable Powder for TBCs Application

This work focuses on the fabrication of lanthanum cerate (La₂Ce₂O₇, LC) powders via two chemical routes: modified Pechini sol-gel method and solid-state synthesis. The synthesized LC powders were heat treated in the temperature range of 1000-1400 °C for 6 h and investigated as a material for thermal barrier coating (TBC) applications. For this purpose, the powder morphology, chemical composition, crystal structure and thermal stability were studied. Scanning electron microscopy (SEM) of the synthesized powders revealed an agglomerated structure consisting of fine and uniformly distributed grains. Energy-dispersive X-ray spectroscopy (EDXS) indicated that the chemical compositions of the LC powders were similar to the stoichiometric ratio of La₂Ce₂O₇. A cubic fluorite structure was observed by X-ray diffraction analysis (XRD) after calcining the LC powder prepared by solid-state synthesis at 1300 °C. In contrast, there was always a fluorite structure in the LC powder synthesized by the Pechini sol-gel method after heat treatment over the entire temperature range. The thermal behavior of the LC powders was analyzed by differential scanning calorimetry (DSC) and thermogravimetric analysis (TG) in the temperature range of 25-1300 °C. Neither an obvious mass change nor a visible energy change was observed within the tested temperature range, indicating high phase stability of the LC powder and its suitability for TBC applications. Spheroidization on the prepared LC powders was also investigated, revealing that powder size and morphology had a significant impact on the spheroidization efficiency.