Study on Photocatalytic Performance of Ag/TiO₂ Modified Cement Mortar

In this paper, Ag-TiO₂ photocatalysts with different Ag contents (1 mol%-5 mol%) were prepared and applied to cement mortar. The photocatalytic performance of Ag-TiO₂ and photocatalytic cement mortar under UV light and simulated solar light was evaluated. The results showed that Ag loading on the surface of TiO₂ could reduce its band gap width and increase its absorbance in the visible region, and 2% Ag-TiO₂ had the highest photocatalytic activity under UV light, the degradation rate of methyl orange (MO) was 95.5% at 30 min, and the first-order reaction constant k was 0.0980 min^-1, which was 61.7% higher than that of TiO₂, and 5% Ag-TiO₂ had the highest photocatalytic activity under solar light, the degradation rate of methylene blue (MB) was 69.8% at 40 min, and the first-order reaction constant k was 0.0294 min^-1, which was 90.9% higher than that of TiO₂. The photocatalytic mortar prepared by the spraying method has high photocatalytic performance, The MO degradation rate of sample S2 under UV light was 87.5% after 120 min, MB degradation rate of sample S5 under solar light was 75.4% after 120 min. The photocatalytic reaction conforms to the zero-order reaction kinetics, which was 1.5 times-3.3 times higher than that of the mixed samples and has no effect on the mechanical properties of mortar.