Preparation of Rosin-Based Composite Membranes and Study of Their Dencichine Adsorption Properties

In this work, rosin-based composite membranes (RCMs) were developed as selective sorbents for the preparation of dencichine for the first time. The rosin-based polymer microspheres (RPMs) were synthesized using 4-ethylpyridine as a functional monomer and ethylene glycol maleic rosinate acrylate as a crosslinking. RCMs were prepared by spinning the RPMs onto the membranes by electrostatic spinning technology. The optimization of various parameters that affect RCMs was carried out, such as the ratio concentration and voltage intensity of electrospinning membrane. The RCMs were characterized by SEM, TGA and FT-IR. The performances of RCMs were assessed, which included adsorption isotherms, selective recognition and adsorption kinetics. The adsorption of dencichine on RCMs followed pseudo-second-order and adapted Langmuir-Freundlich isotherm model. As for the RCMs, the fast adsorption stage appeared within the first 45 min, and the experimental maximum adsorption capacity was 1.056 mg/g, which is much higher than the previous dencichine adsorbents reported in the literature. The initial decomposition temperature of RCMs is 297 °C, the tensile strength is 2.15 MPa and the elongation at break is 215.1%. The RCMs have good thermal stability and mechanical properties. These results indicated that RCMs are a tremendously promising adsorbent for enriching and purifying dencichine from the notoginseng extracts.