Facile Strategy for Preparing a Rosin-Based Low-k Material: Molecular Design of Free Volume

Low-k dielectrics are urgently needed in modern integrated circuits. The introduction of free volume instead of porous structures has become a powerful strategy to reduce the k value. According to this strategy, the biomass resource rosin-containing hydrogenated phenanthrene ring was introduced into benzocyclobutene (BCB) resin to reduce the k value; then a rosin-based BCB monomer was successfully synthesized. Meanwhile, the BCB monomer without a rosin skeleton was prepared. After converting the monomers into thermo-crosslinked materials, notably that the rosin skeleton has a great influence on the free volume and k value of the material. The fractional free volume and k value of the former are 26% and 2.44, respectively, and those of the latter are 14% and 2.84, respectively. In addition, the distances between molecular chains and the density of the former are 0.60 nm and 1.06 g cm^-3, respectively; those of the latter are 0.56 nm and 1.28 g cm^-3, respectively. These data show that introducing hydrogenated phenanthrene rings occupies part of the space and hinders the packing of molecular chains, which increases the distance between molecular chains and reduces the density of the polymer, resulting in an increasing free volume and a reducing k value. Notably that introducing hydrogenated phenanthrene rings cannot affect other properties of the material. Therefore, this research indicates that introducing rosin skeletons can prepare high-performance materials, which provide some promising low-k materials for the development of electronics and microelectronics.