Diamond particles in toothpastes: in-vitro effect on the abrasive enamel wear
Blend Hamza1, Aralia Abdulahad2, Thomas Attin2
1Clinic of Orthodontics and Pediatric Dentistry, Center of Dental Medicine, University of Zurich, Plattenstrasse 11, 8032, Zurich, Switzerland. blend.hamza@zzm.uzh.ch.
Background:
Diamond particles have recently been used as abrasives in toothpastes, which raises questions about its abrasive behaviour towards enamel. This study was carried out to investigate the abrasive enamel wear caused by three diamond-loaded toothpastes (Candida White Diamond: CWD, Swiss Smile Diamond Glow: SSDG, Emoform F Diamond: EFD) and to compare it with a traditional toothpaste with silica abrasive (Colgate Total Original CTO).
Methods:
Eighty bovine enamel samples were divided into four groups (n = 20) and brushed for 21,600 cycles (60 cycles/min) for 6 h at 2.5-N brushing force. The abrasive enamel wear was recorded with a contact profilometer. The median and interquartile range (IQR) of the abrasive enamel wear was calculated in each group. Pairwise comparisons were conducted using Wilcoxon signed rank exact test and the p value was adjusted according to Holm. Significance level was set at 0.05.
Results:
Diamond-loaded toothpastes caused statistically significantly higher abrasive wear than the traditional toothpaste (p < 0.0001). SSDG caused statistically significantly higher enamel wear (19.0 µm (11.2)) than CWD (8.4 µm (4.6)) and EFD (7.3 µm (3.9)) (p < 0.0001).
Conclusions:
Diamond-loaded toothpastes cause higher enamel wear than toothpastes with traditional abrasives and also exhibit different abrasivity behaviour compared to each other.