Distribution Law of Corrosion Products in a Marine Chloride Environment

Steel corrosion is the main cause of reinforced concrete cracking. Conventionally, concrete is considered to crack when the circumferential tensile stress reaches the tensile strength of the concrete. However, few analyses have considered the fracture criteria of the internal cross-section of concrete. Based on the von Mises distribution of angle probabilities, this paper proposes a new probability distribution function for investigating the distribution law of corrosion products. The cracking process of experimental samples was numerically analyzed, and the results were consistent with those of the theoretical model. The effect of the dry-wet cycle ratio on the corrosion products was preliminarily investigated by microscopic observation of the reinforced concrete under different dry-wet cycle corrosion environments.