The Effect of Dentifrice on Micro-Hardness, Surface Gloss, and Micro-Roughness of Nano Filled Conventional and...

The aim of the present study was to evaluate the effect of brushing with two whitening dentifrices (Colgate Optic White (COW) and Colgate Optic White Charcoal (COC)) on surface gloss, micro-roughness, and micro-hardness of nanostructured hybrid conventional (Z350) and bulk-fill (Tetric N Ceram bulk-fill) polymer composite. In total, 96 disk samples using two nano-hybrid composite polymers (Z350 and Tetric N Ceram Bulk-fill) were prepared. All specimens were exposed to two different dentifrices (COW and COC), resulting in four main subgroups in the study. Specimens were assessed for surface gloss, micro-roughness (Ra), and micro-hardness using standardized methodology. Means and standard deviations of properties compared using paired t-test, one-way and two-way ANOVA, and post hoc test. The presence of dentifrices did not show any significant difference in micro-hardness values of Z350 (p > 0.05), whereas micro-hardness of bulk-fill composite significantly reduced on dentifrices exposure (p ≤ 0.05). Bulk-fill polymer composite showed significant reduction in gloss after dentifrice exposure (p < 0.05), however, Z350 showed no significant loss of gloss due to dentifrices (p > 0.05). A significant increase in Ra was observed for both resin materials after exposure to dentifrices (COC and COW). Conventional resin composite (Z350) showed comparable surface hardness and gloss before and after dentifrice exposure, however, micro-roughness increased significantly due to dentifrice exposure. Bulk-fill resin (Tetric N Ceram) showed significant loss of micro-hardness and gloss and increase in micro-roughness on dentifrice exposure. Conventional nano-hybrid composite polymer showed better durability in resisting loss of surface properties compared to bulk-fill resin polymer in the present experiment.