The Created Excellent Thermal, Mechanical and Fluorescent Properties by Doping Eu³⁺-Complex-Anchored Carbon Nanotubes...

In the blending process of the composites, the clustering of MWCNTs under high concentration leads to poor dispersion and difficult complexing with luminescent elements. Cyanate ester resins (CERs) have a brittle network structure when cured caused by a conjugation effect that forms a strong emission peak in the ultraviolet-visible region and quenches the luminescent elements of the fluorescent nanofillers. In this paper, by anchoring of the Eu complex (Eu(TTA)₃Phen, ETP) on a surface of longitudinal split unzipped carbon nanotubes (uMWCNTs); fluorescent nanoparticles were prepared as ETP anchor unzipper carbon nanotubes (ETP-uCNTs). Dicyanate ester of bisphenol E (CER-E monomer) is cured to polycyanurate at a lower temperature to achieve a high conversion, promoting a uniform blend with ETP-uCNTs, providing the fluorescence environment with high color purity. Studies show the ETP-uCNTs solve the agglomeration of MWCNTs and improve the interface binding ability. Compared with the pure CER-E, the tensile strength, bending strength and impact strength of CER-E/0.8 wt.% ETP-uCNT hybrid nanocomposites are increased by 94.6%, 92.8% and 101.1%, respectively. The carbon residue rate of CER-E/ETP-uCNTs is up to 47.14% at 800 °C, the temperature of the maximum reaction rate decreases by 67.81 °C, and the partial absorption of ultraviolet light is realized between 200 and 400 nm.