Nanolayered CoCrFeNi/Graphene Composites with High Strength and Crack Resistance

Xiaobin Feng1, Ke Cao2,3, Xiege Huang1

  • 1Hubei Key Laboratory of Theory and Application of Advanced Materials Mechanics, Wuhan University of Technology, Wuhan 430070, China.

Nanomaterials (Basel, Switzerland)
|June 24, 2022
PubMed

Keywords:
crack resistancehigh-entropy alloymonolayer graphenenanolayered compositesstrength

More Related Videos

Advanced Self-Healing Asphalt Reinforced by Graphene Structures: An Atomistic Insight08:03

Advanced Self-Healing Asphalt Reinforced by Graphene Structures: An Atomistic Insight

Published on: May 31, 2022

4.6K
Graphene Coatings for Biomedical Implants13:21

Graphene Coatings for Biomedical Implants

Published on: March 1, 2013

21.4K

Related Concept Videos

Network Covalent Solids02:18

Network Covalent Solids

Network covalent solids contain a three-dimensional network of covalently bonded atoms as found in the crystal structures of nonmetals like diamond, graphite, silicon, and some covalent compounds, such as silicon dioxide (sand) and silicon carbide (carborundum, the abrasive on sandpaper). Many minerals have networks of covalent bonds.
To break or to melt a covalent network solid, covalent bonds must be broken. Because covalent bonds are relatively strong, covalent network solids are typically...
14.4K
Types of Non-structural Cracks in Concrete01:28

Types of Non-structural Cracks in Concrete

Non-structural cracks are primarily of three types: plastic, early-age thermal, and drying shrinkage cracks. Plastic cracks are further classified into plastic shrinkage cracks and plastic settlement cracks.
Plastic shrinkage cracks typically form within hours after the concrete is poured. The concrete's surface dries faster than the bottom, creating tensile stress that the still-plastic concrete cannot withstand, leading to diagonal or randomly patterned cracks on the concrete surface.
243
Tensile Strength Considerations of Concrete01:16

Tensile Strength Considerations of Concrete

Considering the tensile strength of concrete involves recognizing that the theoretical strength of cement paste can be up to a thousand times higher than what is observed in practical applications. This significant discrepancy is largely attributed to the presence of microscopic cracks within the concrete. These cracks tend to amplify stress at their tips when a load is applied, a phenomenon explained by Griffith's theory of brittle fracture.
The dimensions and shape of a concrete specimen...
193
Yield Criteria for Ductile Materials under Plane Stress01:25

Yield Criteria for Ductile Materials under Plane Stress

In designing structural elements and machine parts using ductile materials, it is crucial to ensure that these components withstand applied stresses without yielding. Yielding is initially determined through a tensile test, which evaluates the material's response to uniaxial stress. However, tensile stress is insufficient when components face biaxial or plane stress conditions This condition requires advanced criteria to predict failure.
The Maximum Shearing Stress Criterion, also known as...
212