Bidimensional Engineered Amorphous a-SnO₂ Interfaces: Synthesis and Gas Sensing Response to H₂S and Humidity

Two-dimensional (2D) transition metal dichalcogenides (TMDs) and metal chalcogenides (MCs), despite their excellent gas sensing properties, are subjected to spontaneous oxidation in ambient air, negatively affecting the sensor's signal reproducibility in the long run. Taking advantage of spontaneous oxidation, we synthesized fully amorphous a-SnO₂ 2D flakes (≈30 nm thick) by annealing in air 2D SnSe₂ for two weeks at temperatures below the crystallization temperature of SnO₂ (T < 280 °C). These engineered a-SnO₂ interfaces, preserving all the precursor's 2D surface-to-volume features, are stable in dry/wet air up to 250 °C, with excellent baseline and sensor's signal reproducibility to H₂S (400 ppb to 1.5 ppm) and humidity (10-80% relative humidity (RH)) at 100 °C for one year. Specifically, by combined density functional theory and ab initio molecular dynamics, we demonstrated that H₂S and H₂O compete by dissociative chemisorption over the same a-SnO₂ adsorption sites, disclosing the humidity cross-response to H₂S sensing. Tests confirmed that humidity decreases the baseline resistance, hampers the H₂S sensor's signal (i.e., relative response (RR) = R_a/R_g), and increases the limit of detection (LOD). At 1 ppm, the H₂S sensor's signal decreases from an RR of 2.4 ± 0.1 at 0% RH to 1.9 ± 0.1 at 80% RH, while the LOD increases from 210 to 380 ppb. Utilizing a suitable thermal treatment, here, we report an amorphization procedure that can be easily extended to a large variety of TMDs and MCs, opening extraordinary applications for 2D layered amorphous metal oxide gas sensors.