Development and Assessment of Bioactive Coatings for the Prevention of Recurrent Caries Around Resin Composite...

To develop hydrophilic resin-based surface coatings containing bioactive agents (proanthocyanidins from Vitis vinifera and calcium silicate) and assess their protective role at the dentin and enamel margins of cervical restorations against demineralization under simulated conditions of high and low caries activity.

Suboptimal resin composite restorations were placed on cervical cavity preparations on buccal and lingual surfaces of thirty-two molars after a contamination protocol. Groups were divided according to the resin-based coatings (n=8): resin without bioactive (C), resin containing 2% enriched Vitis Vinifera (VVE), and resin coat containing 10% calcium silicate (CaSi). The control group did not receive a resin (NC). To simulate a hydrolyticenzymatic degradation, specimens were subjected to 2-month storage followed by incubation in esterase at 37°C for 8 days. Afterwards, recurrent caries was induced using a pH-proteolytic model on half of the specimens to simulate high caries activity, and the other half remained in simulated body fluid (SBF). Measurements of cross-section microhardness (KHN) and infiltration with rhodamine-B assessed the micropermeability (MP), the extent of demineralization (ED), and the demineralization area (DA). Data were analyzed using analysis of variance (ANOVA) and post-hoc tests (α=0.05).

VVE and CaSi presented higher cross-sectional KHN values for enamel and dentin (p<0.001). The bioactive coatings resulted in lower MP, ED, and DA compared to NC (p<0.005) in enamel and dentin. CaSi coating preserved the enamel from demineralization (p=0.160).

The application of bioactive coatings represents a potential strategy to protect the enamel-dentin margins of resin restorations.