Effect of different coatings on the structure and performance of three-dimensional ordered macropores La0.7Ce0.3CoO3
Xinyi Lv1, Tianjiao Zhang1, Jiawei Cao1
1College of Chemistry and Chemical Engineering, China University of Petroleum (East China), Qingdao, 266580, People's Republic of China.
Abstract:
In this work, monolithic catalysts with single coating Ce0.75Zr0.25O2, Al2O3 and composite coating Ce0.75Zr0.25O2-Al2O3 were prepared by PMMA hard template-excessive impregnation method with 3DOM La0.7Ce0.3CoO3 as the active component and cordierite as the carrier, and characterized by SEM, XRD, BET, H2-TPR, and XPS, and the catalytic performance for toluene was tested. The results showed that the active components of 3DOM La0.7Ce0.3CoO3/Ce0.75Zr0.25O2-Al2O3/cordierite catalyst were highly dispersed, forming a complete macroporous structure with the largest specific surface area (10.57 m2·g-1), high surface adsorbed oxygen concentration, and good low-temperature reducibility. Its catalytic activity (T50% = 103℃, T90% = 218℃) for toluene was obviously better than the others. According to the comprehensive analysis, the improvement of the performance of the catalyst may benefit from the excellent physicochemical properties and the synergistic effect between Ce0.75Zr0.25O2-Al2O3 composite coating and active components.