Hierarchical Ti₃C₂T_x@BPA@PCL for flexible polyurethane foam capable of anti-compression, self-extinguishing and...

It is of great importance to fabricate flexible polyurethane foam (FPUF) with superior mechanical properties and flame retardancy for practical applications. Herein, organosilicon and phenyl phosphorus compounds were synthesized and grafted on the surface of Ti₃C₂T_x (Ti₃C₂T_x@BPA@PCL) via in-situ polymerization. Then, the FPUF composites were fabricated, combining intrinsic flame retardancy (9,10-dihydro-9-oxa-10-phosphaphenanthrene 10-oxide-diethanolamine: DH-DOPO) (addition amount: 20 wt%) and Ti₃C₂T_x@BPA@PCL (addition amount: 4 wt%). Attributed to the rigid structure of Ti₃C₂T_x@BPA@PCL, the tensile strength and compression strength of FPUF showed 24.0% and 253% increase, respectively. In addition, anti-fatigue properties of FPUF composites during the cyclical test were dramatically enhanced. In contrast to pure FPUF, 36.1% and 44.0% reductions in peak heat release rate (pHRR) and total heat release (THR) were achieved for the FPUF containing Ti₃C₂T_x@BPA@PCL and DH-DOPO, the production rate of carbon dioxide (CO₂) and carbon oxide (CO) also decreased by 40.3% and 52.1%, respectively. FPUF4 showed self-extinguishing behavior, and passed the vertical burning test (VBT). This work provides a facile approach to preparing high-performance FPUF with enhanced mechanical property and flame retardancy.