Rhombohedral Phase Formation in Yttria-Stabilized Zirconia Induced by Dental Technical Tools and Its Impact on Dental...

In the study the influence of different dental technical tools on the surface temperature and phase composition of fixed dental prostheses (FDPs) made of yttria-partially stabilized zirconia polycrystals (3Y-/4Y-/5Y-PSZ) was investigated. FDPs were fabricated by using computer-aided manufacturing (CAM). The FDPs were treated with a contra-angle handpiece equipped with different burs and polishers. The resulting surface temperatures were measured with a thermographic camera, and the resulting phase transformations were investigated by X-ray diffraction and quantified by Rietveld refinement. Processing with burs resulted in no phase transformation, but a preferred orientation shift. Using coarse polisher induced a phase transformation to the rhombohedral phase, while fine polishers produced no relevant phase transformations and no preferred orientation shift. Compared to the monoclinic phase (ca. 9% theoretical volume increase), which is associated with low-temperature degradation (LTD), the rhombohedral phase is much more voluminous (ca. 15% theoretical volume increase) and distorted and, therefore, has a greater degradation potential.