Study on Increasing the Binding Amount of Rubber and Reinforcing Filler by Adding Aromatic Solvent Oil

The binding amount of rubber and reinforcing filler directly affects the quality of rubber products. The effect of aromatic solvent oil (S-150) on the binding amount of rubber and reinforcing filler was studied. In order to determine the suitability of rubber after adding S-150, the curing characteristics, physical performance and tensile properties of rubber samples were tested and analyzed. Meanwhile, the microstructure of the composite was analyzed by scanning electron microscopy (SEM). The test results showed that the binding amount of rubber and reinforcing filler was increased after adding S-150. The density and Shore A hardness were decreased. When carbon black was 80 phr, after adding 40 phr of S-150, the rebound resilience of rubber increased by 13% on average, and the elongation at break increased by 88% on average. When white carbon black was between 10-70 phr, after adding 65 phr of S-150, the rebound resilience of rubber increased by 9% on average, and the elongation at break increased by 51% on average. Modulus at 100% and tensile strength were decreased. Meanwhile, it could be judged from the microstructure results that the reticulation space inside the rubber was increased, the agglomerate particles were relatively uniform, and no bubbles or holes were observed. The mechanism that S-150 could increase the binding amount of rubber was analyzed according to the like-dissolves-like principle. This research achievement could lead to improvements in the quality of rubber products and promote their practical application.