Effect of three aging processes on physicochemical and As(V) adsorption properties of Ce/Mn-modified biochar

Modified biochar used for soil remediation is affected by exposure to the environment and aging process results in changes in its physicochemical properties and As(V) adsorption and immobilization in soil. Herein, the Ce/Mn-modified wheat straw-biochar (MBC) was manufactured and then aged through three artificial aging processes by exposure to soil with additional natural, freeze-thaw, and dry-wet cycles involved. It revealed that the specific surface areas of freeze-thaw-aged MBC reached 214.98 m²/g and was increased more than those of other two aging treatments. In addition, the pH values and C contents of MBC all decreased after aging while the H and O contents increased. Correspondingly, the contents of O-containing functional groups like C-O, -OH, and CO all increased by >16% with aging. The freeze-thaw cycling and alternating dry-wet aging treatments improved adsorption capacities of As(V) onto MBC and were increased by 16.2 and 10.6% at pH 5, respectively and these samples exhibited the best recyclability and adsorption selectivity for As(V). However, natural aging exerted a lower effect for As(V) adsorption by MBC due to its few changes on physicochemical properties. Causally, the freeze-thaw and dry-wet aging activated the Ce/Mn-oxides to generate Mn^2+/3+ species and a new mono-Ce that exerted a strong bonding complexation with As(V) to form Ce/Mn-O-As ligands and increased CeAsO₄ precipitation. Our results offer a new insight into the alterations expected for modified biochars with aging treatment in terms of As(V) adsorption for its long-term utilization in As contaminated soil.