Producing submicron chitosan-stabilized oil Pickering emulsion powder by an electrostatic collector-equipped spray
Meisam Tabatabaei1, Behnam Ebrahimi2, Ahmad Rajaei2
1Henan Province Engineering Research Center for Forest Biomass Value-added Products, School of Forestry, Henan Agricultural University, Zhengzhou 450002, China; Higher Institution Centre of Excellence (HICoE), Institute of Tropical Aquaculture and Fisheries (AKUATROP), Universiti Malaysia Terengganu, 21030 Kuala Nerus, Terengganu, Malaysia; Biofuel Research Team (BRTeam), Terengganu, Malaysia.
Abstract:
Chitosan (CS) was modified with two fatty acids, i.e., capric acid (CA) and palmitic acid (PA). Particle size (315.8 nm), zeta potential (31.8 mV), and viscosity (29.4 mPa.s) of CS-PA nanogels were lower than CS-CA nanogels (793.2 nm, 53.3 mV, and 70.7 mPa.s). First, hempseed oil-in-water Pickering nanoemulsions were stabilized by CS-based particles/maltodextrin (MD). Then, the emulsions were dried using an electrostatic collector-equipped spray dryer. The D50 of re-dispersed emulsion powders with CS-PA/MD coating was 936 nm. According to the FE-SEM images, oil coated with CS-PA/MD showed higher porosity and C/O ratio at the particle surface compared to the CS-CA/MD coating leading to more oil leakage. In addition, the crystallinity of hempseed oil coated with CS-PA/MD was higher than the one coated with CS-CA/MD. These findings showed that submicron Pickering emulsion powders could be achieved by targeted modification of CS and using a spray dryer equipped with an electrostatic collector.