Antimony Nanoparticles Encapsulated in Self-Supported Organic Carbon with a Polymer Network for High-Performance
Zhaomin Wang1,2, Fanming Zeng1,2, Dongyu Zhang3
1School of Materials Science and Engineering, Changchun University of Science and Technology, Changchun 130022, China.
Abstract:
Antimony (Sb) demonstrates ascendant reactive activation with lithium ions thanks to its distinctive puckered layer structure. Compared with graphite, Sb can reach a considerable theoretical specific capacity of 660 mAh g-1 by constituting Li3Sb safer reaction potential. Hereupon, with a self-supported organic carbon as a three-dimensional polymer network structure, Sb/carbon (3DPNS-Sb/C) composites were produced through a hydrothermal reaction channel followed by a heat disposal operation. The unique structure shows uniformitarian Sb nanoparticles wrapped in a self-supported organic carbon, alleviating the volume extension of innermost Sb alloying, and conducive to the integrality of the construction. When used as anodes for lithium-ion batteries (LIBs), 3DPNS-Sb/C exhibits a high invertible specific capacity of 511.5 mAh g-1 at a current density of 0.5 A g-1 after 100 cycles and a remarkable rate property of 289.5 mAh g-1 at a current density of 10 A g-1. As anodes, LIBs demonstrate exceptional electrochemical performance.