Biodegradable Films Prepared from Pulp Lignocellulose Adhesives of Urea Formaldehyde Resin Modified by Biosulfonate

Traditional low-density polyethylene (LDPE) film causes environmental pollution; there is a pressing need to make new bio-based polymers for alternative products, to meet agricultural production needs and for sustainable ecological development. In this study, urea-formaldehyde resin (UF) was modified with polyvinyl alcohol (PVA) and 1-2.5% bio-based sulfonate (BBS). The influence of BBS inducing on the functional groups, microstructure, and thermal behavior was evaluated by Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA). A biodegradable film was prepared with modified UF resin as adhesive and pulp lignocellulose as raw material. The biodegradable mulch film samples were tested for biodegradability, water retention, and cooling soil temperature characters using LDPE and no mulching (NM) as a control. The results showed that with the increase of BBS content, the viscosity and reactivity of modified PUF resin increased, and the free formaldehyde content decreased. A 2%BBS modified PUF resin (2.0BBS/PUF) accelerated the curing process of the PUF resin, formed a flexible macromolecular network structure, and enhanced the toughness of the resin. The biodegradable mulch prepared with PUF, BBS, and 2.0BBS/PUF as adhesives had good water retention. BBS modification increased the degradation rate of mulch by 17.53% compared to the PUF. Three biodegradable films compared with LDPE and NM significantly reduced the soil temperature under summer cucumber cultivation, and the 2.0BBS/PUF coating had the lowest diurnal temperature difference, which provided a suitable soil environment for crop growth.