Utilization of Sulfonated Waste Polystyrene-Based Cobalt Ferrite Magnetic Nanocomposites for Efficient Degradation of...

We presented a simple and efficient method for making a polymer-metal nanocomposite using various amounts of cobalt ferrite magnetic nanoparticles (CoFe₂O₄ MNp) with sulfonated waste polystyrene (SWPS) and utilized for Calcon dye degradation. The MNp was encapsulated with SWPS to avoid agglomeration and maintain its smaller size. ATR-FTIR, Raman spectroscopy, X-ray diffraction (XRD), thermogravimetric analysis (TGA), dynamic light scattering (DLS), field emission scanning electron microscopy (FESEM), high-resolution transmittance electron microscopy (HR-TEM), atomic force microscopy (AFM) and solid UV were used to analyze the produced polymeric magnetic nanoparticles (SWPS/MNp). As the MNp loading increases, the average particle size decreases. For Calcon dye degradation, SWPS/MNp (20 wt%) was utilized with a smaller average particle size, and the structural changes were detected using a UV-Vis spectrophotometer. As a result, the Calcon dye's characteristic absorbance peak at 515 nm was red-shifted to 536 and 565 nm after 5 min, resulting in a color shift from dark brown to light blue that could be seen with the naked eye. A strong linear correlation was found between the red-shifted absorbance and the concentration of dye solution over the range of 10-100 ppm under optimal conditions. The proposed dye degradation process is simple, efficient, and environmentally friendly and has been successfully used to purify organic azo-dye-containing water.