Corrosion Behavior of Friction Stir Welded AA8090-T87 Aluminum Alloy

Aerospace alloys with reduced wall thickness but possessing higher hardness, good tensile strength and reasonable corrosion resistance are essential in manufacturing of structures such as fuselage. In this work, friction stir welding has been carried out on such an aerospace aluminum alloy AA8090 T87 which contains 2.3% lithium. Tool rotational speed of 900 rpm and traverse speeds of 90 mm/min., 110 mm/min. are the welding parameters. Hardness analysis, surface roughness analysis and corrosion analysis are conducted to analyze the suitability of the joint for the intended application. The samples were corrosion tested in acid alkali solution and they resulted in the formation of pits of varying levels which indicate the extent of surface degradation. Hardness of the samples was measured after corrosion analysis to observe the changes. The analysis suggests that the change in tool traverse speed transformed the corrosion behavior of the joint and affected both the hardness and surface roughness which mitigated the quality of the joint.